20Cr2Ni4A Φ12MM（軋材）軍工鋼?
20Cr2Ni4A Φ16MM（軋材）軍工鋼?
20Cr2Ni4A Φ20MM（軋材）軍工鋼?
20Cr2Ni4A Φ22MM（軋材）軍工鋼?
20Cr2Ni4A Φ25MM（軋材）軍工鋼?
20Cr2Ni4A Φ30MM（軋材）軍工鋼?
20Cr2Ni4A Φ32MM（軋材）軍工鋼?
20Cr2Ni4A Φ35MM（軋材）軍工鋼?
20Cr2Ni4A Φ40MM（軋材）軍工鋼?
20Cr2Ni4A Φ42MM（軋材）軍工鋼?
20Cr2Ni4A Φ45MM（軋材）軍工鋼?
20Cr2Ni4A Φ50MM（軋材）軍工鋼?
20Cr2Ni4A Φ55MM（軋材）軍工鋼?
20Cr2Ni4A Φ60MM（軋材）軍工鋼?
20Cr2Ni4A Φ65MM（軋材）軍工鋼?
20Cr2Ni4A Φ70MM（軋材）軍工鋼?
20Cr2Ni4A Φ75MM（軋材）軍工鋼?
20Cr2Ni4A Φ80MM（軋材）軍工鋼?
20Cr2Ni4A Φ85MM（軋材）軍工鋼?
20Cr2Ni4A Φ90MM（軋材）軍工鋼?
20Cr2Ni4A Φ95MM（軋材）軍工鋼?
20Cr2Ni4A Φ100MM（鍛材）軍工鋼?
20Cr2Ni4A Φ110MM（鍛材）軍工鋼?
20Cr2Ni4A Φ120MM（鍛材）軍工鋼?
20Cr2Ni4A Φ130MM（鍛材）軍工鋼?
20Cr2Ni4A Φ140MM（鍛材）軍工鋼?
20Cr2Ni4A Φ150MM（鍛材）軍工鋼?
20Cr2Ni4A Φ160MM（鍛材）軍工鋼?
20Cr2Ni4A Φ170MM（鍛材）軍工鋼?
20Cr2Ni4A Φ180MM（鍛材）軍工鋼?
20Cr2Ni4A Φ190MM（鍛材）軍工鋼?
20Cr2Ni4A Φ200MM（鍛材）軍工鋼?
20Cr2Ni4A Φ210MM（鍛材）軍工鋼?
20Cr2Ni4A Φ220MM（鍛材）軍工鋼?
20Cr2Ni4A Φ230MM（鍛材）軍工鋼?
20Cr2Ni4A Φ240MM（鍛材）軍工鋼?
20Cr2Ni4A Φ250MM（鍛材）軍工鋼?
20Cr2Ni4A Φ260MM（鍛材）軍工鋼?
20Cr2Ni4A Φ270MM（鍛材）軍工鋼?
20Cr2Ni4A Φ280MM（鍛材）軍工鋼?
20Cr2Ni4A Φ290MM（鍛材）軍工鋼?
20Cr2Ni4A Φ300MM（鍛材）軍工鋼?
======================
上海高高商貿(mào)有限公司：
：
br>QQ:404914802
聯(lián)系人：粟太成
地址：上海市寶山區(qū)撫遠路1288弄61號
==================================
材料名稱：合金結(jié)構(gòu)鋼（軍工鋼）
牌號：20Cr2Ni4A
20Cr2Ni4A特性及適用范圍：
是**合金鋼，強度高，韌性及淬透性好。滲碳后不能直接淬火，以減少表層殘余奧氏體。切削性及冷變形塑性一般。焊接性較差，焊前需預(yù)熱到150℃左右，工時白點敏感性強，有回火脆性傾向。用于大截面滲碳件，如大型齒輪、軸類以及要求強度高、韌性好的調(diào)質(zhì)零部件等。
20Cr2Ni4A化學(xué)成份：
碳 C ：0.17～0.23
硅 Si：0.17～0.37
錳 Mn：0.30～0.60
硫 S ：≤0.03
磷 P ：≤0.03
鉻 Cr：1.25～1.65
鎳 Ni：3.25～3.65
20Cr2Ni4A力學(xué)性能：
抗拉強度 σb (MPa)：1483
條件屈服強度 σ0.2 (MPa)：1292
伸長率 δ5 (％)：13
斷面收縮率 ψ (％)：57
沖擊韌性值 αkv (J/cm2)：75
硬度 ：434HB
試樣尺寸：某試料
20Cr2Ni4A熱處理規(guī)范及金相組織：
熱處理規(guī)范：880℃油淬+780℃油淬,200℃回火。
金相組織：回火馬氏體。
20Cr2Ni4A合金結(jié)構(gòu)鋼（軍工鋼）以上由上海高高特鋼自行發(fā)行，如有對20Cr2Ni4A合金結(jié)構(gòu)鋼（軍工鋼）不詳之處，敬請來電洽談！高高特鋼將以真信息、真品質(zhì)、真價格的為您提供20Cr2Ni4A合金結(jié)構(gòu)鋼（軍工鋼）有關(guān)環(huán)節(jié)！