SEBS Thermoplastic elastomer

熱塑性橡膠SEBS產(chǎn)品耐老化性能優(yōu)良，廣泛用于高彈性制品、包履材料（工具手柄）、聚合物改性、膠粘劑與密封劑、醫(yī)療器械、電線電纜的填充料等。

SEBS is of excellent aging resistance and used for highly elastic products, packing material (tool handles) polymer modification,adhesives,sealant,meddical treatment equipment and fillers of wires and cables.

SEBS具有較好的耐溫性能，其脆化溫度≤－60℃，*時(shí)使用溫度達(dá)到149℃，在氧氣氣氛下其分解溫度大于270℃。SEBS有優(yōu)異的耐老化性能，在人工加速老化箱中老化一星期其性能的下降率小于10%。SEBS有優(yōu)良的電性能，其介電損耗在一千赫為1.3×10，一兆赫為2.3×10；體積電阻是一分鐘9×10Ω-cm,二分鐘2×10Ω-cm。SEBS具有良好的溶解性能和共混性能，其溶解度參數(shù)在7.2-7.6之間。

SEBS is of good temperature endurance with brittle temperature lower than-60℃and highest service temperature at149℃,Under oxygen surround. The decomposing point is higher than270℃.SEBS has excellent aging resistance and the drop rate of its performance is less than 10% after being aged in the artificial aging accelerator for one week.

SEBS is also very good at electrical property Its dielectric loss is 1.3×10 at 1KHZ and 2.3×10 at 1MHZ; its volume resistance is 9×10Ω-cm one minute and 2×10Ω-cm two minutes. SEBS has good solubility and co-mixing capacity with solubility between 7.2～7.6.

主要牌號(hào)有：YH-501、YH-502、YH-503、YH-561、YH-602

注：*20%甲苯溶液 ^10%甲苯溶液

● SEBS通過與聚丙烯、環(huán)烷油或氫化環(huán)烷油、白油等混合可生產(chǎn)邵A0-95度的彈性體，此類彈性體有優(yōu)異的表面質(zhì)感和耐候抗老化性能，可廣泛用于軟接觸材料如手柄、文具、玩具、運(yùn)動(dòng)器材的握手、密封條、電線電纜、牙刷柄及其它包覆材料等。

● SEBS通過化學(xué)改性或共混于增韌尼龍（PA6）、聚碳酸脂（PC）聚苯醚（PPO）聚脂（PET、PBT）、聚丙烯（PP）作塑料共混的相容劑等。

● SEBS可用作工程塑料的相容劑，如作PE與PS相容劑。

● SEBS與聚丙烯、白油阻燃劑等共混可用于生產(chǎn)電線電纜的護(hù)套或外表皮。

● SEBS通過與碳五等石油樹脂配合可用于生產(chǎn)**粘膠劑、密封劑。

● SEBS具有耐老化性能，可直接用于潤滑油粘度指數(shù)穩(wěn)定劑。